ELX1414-耐低温PC-耐寒PC-LEXAN

产品参数

特性				单位	检测标准
	EXL1414	EXL1414H	EXL1414T
Tensile Stress, yld, Type I,50 mm/min	55	56	57	MPa	ASTM D638
Tensile Stress, brk, Type I,50 mm/min	50	50	59	MPa	ASTM D638
Tensile Strain, yld, Type I, 50mm/min	6	6	5.6	%	ASTM D638
Tensile Strain, brk, Type I,50 mm/min	98	98	123.9	%	ASTM D638
Tensile Modulus,50 mm/min	2020	2020	2180	MPa	ASTM D638
Flexural Stress, yld,1.3 mm/min, 50mm span	92	92	0.15	MPa	ASTM D790
Flexural Modulus,1.3 mm/min,50 mm span	2230	2230	2.5	MPa	ASTM D790
Hardness, Rockwell L	89	-	87	-	ASTM D785
Hardness, Rockwell R	121	-	-	-	ASTM D785
Izod Impact, notched,23°C	865	865	824	J/m	ASTM D256
Izod Impact, notched,-30°C	774	774	712	J/m	ASTM D256
Instrumented Dart Impact Total Energy,23°C	70	70	75	J	ASTM D3763
Instrumented Dart Impact Total Energy,-30°C	-	77	77	J	ASTM D3763
Vicat Softening Temp, Rate B/50	145	145	138	°C	ASTM D1525
HDT,0.45 MPa,3.2 mm, unannealed	139	139	-	°C	ASTM D648
HDT,1.82 MPa,3.2mm, unannealed	124	124	120	°C	ASTM D648
CTE,-40°C to 40°C, flow	7.0E-05	7.0E-05	-	1/°C	ASTM E831
CTE,-40°C to 40°C, xflow	7.47E-05	7.0E-05	-	1/°C	ASTM E831
Ball Pressure Test,125°C +/-2°C	Passes	Passes	Passes	-	IEC 60695-10-2
Relative Temp Index, Elec	130	-	-	°C	UL 746B
Relative Temp Index, Mech w/impact	120	-	-	°C	UL 746B
Relative Temp Index, Mech w/o impact	130	-	-	°C	UL 746B
PHYSICAL
Specific Gravity	1.18	1.18	1.19	-	ASTM D792
Mold Shrinkage, flow,3.2 mm	0.4-0.8	0.4-0.8	0.4-0.8	%	SABIC method
Mold Shrinkage, xflow,3.2 mm	0.4-0.8	-	0.4-0.8	%	SABIC method
Melt Flow Rate,300°C/1.2 kgf	10	10	10	g/10 min	ASTM D1238
ELECTRICAL
Volume Resistivity	>1.E+15	-	>1.E+15	Ω.cm	ASTM D257
Surface Resistivity	>1.E+15	-	>1.E+15	Ω	ASTM D257
Dielectric Strength, in oil,0.8mm	16.2	-		kV/mm	ASTM D149
Relative Permittivity,100Hz	2.68	-		-	ASTM D150
Relative Permittivity,1MHz	2.64	-		-	ASTM D150
Dissipation Factor,100Hz	0.0012	-		-	ASTM D150
Dissipation Factor,1 MHz	0.0093	-		-	ASTM D150
Hot-Wire Ignition (HWI), PLC 0	≥0.7	-		mm	UL 746A
High Amp Arc Ignition (HAI),PLC 1	≥0.7	-	≥1.5	mm	UL 746A