特性

单位

检测标准

143R

Tensile Stress, yield, 50mm/min

63

MPa 

ISO 527

70

MPa 

ISO 527

6

%

110

ISO 527

Tensile Modulus, 1 mm/min

2350

MPa 

ISO 527

Flexural Stress, yield, 2 mm/min 

90

MPa 

ISO 178

Flexural Modulus, 2 mm/min 

2300

MPa 

ISO 178

Ball Indentation Hardness, H358/30 

95

MPa 

ISO 2039-1

IMPACT

Izod Impact, unnotched 80*10*3 +23°C 

NB

kJ/m²

ISO 180/1U

Izod Impact, unnotched 80*10*3 -30°C

NB

kJ/m² 

ISO 180/1U

Izod Impact, notched 80*10*3 +23°C

70

kJ/m²

ISO 180/1A

Izod Impact, notched 80*10*3 -30°C

 12

kJ/m²

ISO 180/1A

Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm 

73

kJ/m²

ISO 179/1eA

Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm  

14

kJ/m²

ISO 179/1eA

Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm 

NB

kJ/m² 

ISO 179/1eU

Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm 

NB

kJ/m²

ISO 179/1eU

Charpy Impact, notched,23°C 

35

kJ/m²

ISO 179/2C

THERMAL

Thermal Conductivity

0.2

W/m-°C

ISO 8302

CTE,23°C to 80°C, xflow 

7.E-05

1/°C 

ISO 11359-2

Ball Pressure Test,125°C +/-2°C 

PASSES 

-

IEC 60695-10-2

Vicat Softening Temp, Rate B/50 

141

°C

ISO 306

Vicat Softening Temp, Rate B/120

141

142

°C

ISO 306 

HDT/Be,0.45MPa Edgew 120*10*4 sp=100mm

HDT/Ae,1.8 MPa Edgew 120*10*4 sp=100mm 

Relative Temp Index, Elec

Relative Temp Index, Mech w/impact 

PHYSICAL

Mold Shrinkage on Tensile Bar, flow 

Density

Water Absorption, (23°C/saturated) 

Moisture Absorption (23°C / 50% RH) 

Dissipation Factor,100Hz 

Dissipation Factor,1 MHz

Melt Volume Rate, MVR at 300°C/1.2 kg 

Light Transmission,2.54mm 

88–90

%

ASTM D1003