TYPICAL PROPERTIES1

TYPICAL VALUE

UNIT

STANDARD

MECHANICAL

Tensile Stress, brk, Type I, 5 mm/min

119

MPa

ASTM D 638

Tensile Strain, brk, Type I, 5 mm/min

2.6

%

ASTM D 638

Tensile Modulus, 5 mm/min

7100

MPa

ASTM D 638

Flexural Stress, brk, 1.3 mm/min, 50 mm span

175

MPa

ASTM D 790

Flexural Modulus, 1.3 mm/min, 50 mm span

6970

MPa

ASTM D 790

Taber Abrasion, CS-17, 1 kg

65

mg/1000cy

SABIC Method

Tensile Stress, break, 5 mm/min

119

MPa

ISO 527

Tensile Strain, break, 5 mm/min

2.6

%

ISO 527

Tensile Modulus, 1 mm/min

7170

MPa

ISO 527

Flexural Stress, break, 2 mm/min

165

MPa

ISO 178

Flexural Modulus, 2 mm/min

6040

MPa

ISO 178

Hardness, H358/30

220

MPa

ISO 2039-1

IMPACT

lzod Impact, unnotched, 23°C

400

J/m

ASTM D 4812

lzod Impact, unnotched, -30°C

395

J/m

ASTM D 4812

lzod Impact, notched, 23°C

65

J/m

ASTM D 256

lzod Impact, notched, -30°C

45

J/m

ASTM D 256

lzod Impact, notched, -30°C

25

kJ/m²

ISO 180/1U

lzod Impact, notched, -30°C

23

kJ/m²

ISO 180/1U

lzod lmpact, notched 80*10*4 +23°C

6

kJ/m²

ISO 180/1A

lzod lmpact, notched 80*10*4 +23°C

4

kJ/m²

ISO 180/1A

Charpy Impact, notched, 23°C

6

kJ/m²

ISO 179/2C

Charpy -30C, V-notch Edgew 80* 10*4 sp=62mm

5

kJ/m²

ISO 179/1eA

Charpy Impact, notched, -30°C

27

kJ/m²

ISO 179/2C

Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm

30

kJ/m²

ISO 179/1eU

THERMAL

HDT.1 82 MPa. 3 2mm. nannealed

135

°C

ASTM D 648