TYPICAL PROPERTIES¹

TYPICAL VALUE

UNIT

STANDARD

MECHANICAL

Tensile Stress,yld, Type I, 50 mm/min

55

MPa

ASTM D 638

Tensile Strain, brk, Type I, 50 mm/min

50

MPa

ASTM D 638

Tensile Strain, yld, Type I, 50 mm/min

6

%

ASTM D 638

Tensile Strain, brk, Type I, 50 mm/min

98

%

ASTM D638

Tensile Modulus, 50 mm/min

2020

MPa

ASTM D638

Flexural Stress, yld, 1.3 mm/min, 50 mm span

92

MPa

ASTM D790

Flexural Modulus, 1.3 mm/min, 50 mm span

2230

MPa

ASTM D790

Hardness, Rockwell L

89

-

ASTM D785

Hardness, Rockwell R

121

-

ASTM D785

Tensile Stress, yield, 50 mm/min

57

MPa

ISO 527

Tensile Stress, break, 50 mm/min

60

MPa

ISO 527

Tensile Strain, yield, 50 mm/min

6

%

ISO 527

Tensile Strain, break, 50 mm/min

120

%

ISO 527

Tensile Modulus, 1 mm/min

2150

MPa

ISO 527

Flexural Stress, yield, 2 mm/min

85

MPa

ISO 178

Flexural Modulus, 2 mm/min

2250

MPa

ISO 178

IMPACT

lzod Impact, unnotched, 23°C

865

J/m

ASTM D256

lzod Impact, unnotched, -30°C

774

J/m

ASTM D256

lzod Impact, notched, 23°C

70

J

ASTM D3763

Izod Impact, unnotched 80*10*3 +23°C

NB

kJ/m²

ISO 180/1U

lzod Impact, notched, -30°C

NB

kJ/m²

ISO 180/1U

Izod Impact, notched 80*10*3 +23°C

70

kJ/m²

ISO 180/1A

lzod Impact, notched, -30°C

60

kJ/m²

ISO 180/1A

Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm

70

kJ/m²

ISO 179/1eA

Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm

65

kJ/m²

ISO 179/1eA

Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm

NB

kJ/m²

ISO 179/1eU

Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm

NB

kJ/m²

ISO 179/1eU

THERMAL

Vicat Softening Temp, Rate B/50

145

°C

ASTM D1525

HDT, 0.45 MPa, 3.2 mm, unannealed

139

°C

ASTM D648

HDT, 1.82 MPa, 3.2mm, unannealed

124

°C

ASTM D648

CTE, -40°C to 40°C, flow

7.0E-05

1/°C

ASTM E831

CTE, -40°C to 40°C, xflow

7.47E-05

1/°C

ASTM E831