特性 |
C4210HF | C4220 |
单位 |
检测标准 |
|
MECHANICAL |
|
|
|
|
|
Tensile Stress, yield, 5 mm/min
|
90 | 90 |
MPa |
ISO 527
|
|
Tensile Stress, break, 5 mm/min
|
90 | 90 |
MPa |
ISO 527
|
|
Tensile Strain, yield, 5 mm/min
|
3.2 | 2.5 |
% |
ISO 527
|
|
Tensile Strain, break, 5 mm/min
|
3.2 | 2.5 |
%
|
ISO 527
|
|
Tensile Modulus, 1 mm/min
|
4700 | 6000 |
MPa |
ISO 527
|
|
Flexural Stress, yield, 2 mm/min
|
125 | - |
MPa
|
ISO 178
|
|
Flexural Stress, break, 2 mm/min
|
135 | 135 |
MPa
|
ISO 178
|
|
Flexural Modulus, 2 mm/min
|
4250 | 5300 |
Mpa |
ISO 178
|
|
Ball Indentation Hardness, H358/30
|
116 |
116 |
MPa |
ISO 2039-1
|
|
Hardness, Rockwell R
|
121 | 121 |
- |
ISO 2039-1
|
|
IMPACT
|
|
|
|
|
|
Izod Impact, unnotched 80*10*3 +23°C
|
20 | 15 |
kJ/m²
|
ISO 180/1U
|
|
Izod Impact, notched 80*10*3 +23°C
|
8 |
8 |
kJ/m² |
ISO 180/1A
|
|
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm
|
8 |
8 |
kJ/m² |
ISO 179/1eA
|
|
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm
|
20 | 15 |
kJ/m² |
ISO 179/1eU
|
|
THERMAL
|
|
|
|
|
|
Thermal Conductivity
|
0.2 | 0.2 |
W/m-°C
|
ISO 8302
|
|
CTE, -40°C to 40°C, flow
|
4.E-05
|
|
1/°C
|
ISO 11359-2
|
|
CTE, -40°C to 40°C, xflow
|
8.E-05
|
|
1/°C
|
ISO 11359-2
|
|
Ball Pressure Test, 75°C +/- 2°C
|
PASSES
|
PASSES |
- |
IEC 60695-10-2
|
|
Ball Pressure Test, 125°C +/- 2°C
|
PASSES
|
PASSES | - |
IEC 60695-10-2
|
|
Vicat Softening Temp, Rate B/50
|
134 | 135 |
°C
|
ISO 306
|
|
Vicat Softening Temp, Rate B/120
|
136 | 137 |
°C
|
ISO 306
|
|
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm
|
133 | 135 |
°C
|
ISO 75/Be
|
|
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm
|
123 |
129 |
°C
|
ISO 75/Ae
|
|
Relative Temp Index, Elec
|
60 | 60 |
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/impact
|
60 | 60 |
°C |
UL 746B
|
|
Relative Temp Index, Mech w/o impact
|
60
|
60
|
°C |
UL 746B
|
|
PHYSICAL
|
|
|
|
|
|
Mold Shrinkage on Tensile Bar, flow
|
0.3-0.5 | 0.2-0.4 | % |
SABIC method
|
|
Density
|
1.22 | 1.3 |
g/cm³
|
ISO 1183
|
|
Water Absorption, (23°C/saturated)
|
0.6 | 0.6 |
%
|
ISO 62-1
|
|
Moisture Absorption (23°C / 50% RH)
|
0.2 |
0.2
|
%
|
ISO 62
|
|
Melt Volume Rate, MVR at 260°C/5.0 kg
|
33 |
12 |
cm³/10 min
|
ISO 1133
|
|
ELECTRICAL
|
|
|
|
|
|
Volume Resistivity
|
>1.E+15
|
>1.E+15
|
Ω.cm
|
IEC 60093
|
|
Surface Resistivity, ROA
|
>1.E+15
|
>1.E+15
|
Ω |
IEC 60093
|
|
INJECTION MOLDING
|
|
|
|
|
|
Drying Temperature
|
100-110 | 100-110 |
°C |
|
|
Drying Time
|
2-4 | 2-4 |
Hrs
|
|
|
Melt Temperature
|
240-280 | 240-280 |
°C |
|
|
Mold Temperature
|
50-80 |
50-80
|
°C
|
|