CYCOLOY™ RESIN-C1200HF-PC/ABS合金-SABIC代理商

产品参数

特性	C1200HF	单位	检测标准
MECHANICAL
Tensile Stress, yld, Type I, 50 mm/min	57	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	5	%	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	100	%	ASTM D638
Tensile Modulus, 50 mm/min	2270	MPa	ASTM D638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	88	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	2340	MPa	ASTM D790
IMPACT
Izod Impact, notched, 23°C	587	J/m	ASTM D256
Izod Impact, notched, -30°C	480	J/m	ASTM D256
Instrumented Dart Impact Total Energy, 23°C	54	J	ASTM D3763
Instrumented Dart Impact Total Energy, -30°C	54	J	ASTM D3763
THERMAL
HDT, 0.45 MPa, 3.2 mm, unannealed	129	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	112	°C	ASTM D648
CTE, -40°C to 40°C, flow	7.2E-05	1/°C	ASTM E831
Vicat Softening Temp, Rate B/50	130	°C	ISO 306
Relative Temp Index, Elec	105	°C	UL 746B
Relative Temp Index, Mech w/impact	80	C	UL 746B
Relative Temp Index, Mech w/o impact	105	°C	UL 746B
PHYSICAL
Specific Gravity	1.15	-	ASTM D792
Mold Shrinkage, flow, 3.2 mm	0.5-0.7	%	SABIC method
Melt Flow Rate, 260°C/5.0 kgf	19	%	ASTM D1238
ELECTRICAL
Hot Wire Ignition {PLC)	3	PLC Code	UL 746A
High Ampere Arc Ign, surface {PLC}	1	PLC Code	UL 746A
Comparative Tracking Index (UL) {PLC}	2	PLC Code	UL 746A
FLAME CHARACTERISTICS
UL Yellow Card Link	E207780-228463		-
UL Yellow Card Link2	E45587-236932	-	-
UL Recognized, 94HB Flame Class Rating	1.19	mm	UL94
INJECTION MOLDING
Drying Temperature	100-110	°C
Drying Time	3-4	Hrs
Drying Time (Cumulative)	8	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	275-300	°C	UL 746A
Nozzle Temperature	275-300	°C
Front - Zone 3 Temperature	260-300	°C
Middle - Zone 2 Temperature	255-295	°C
Rear - Zone 1 Temperature	250-290	°C
Hopper Temperature	60-80	°C
Mold Temperature	60-90	°C
Back Pressure	0.3-0.7	MPa
Screw Speed	40-70	rpm
Shot to Cylinder Size	30-80	%
Vent Depth	0.038-0.076	mm